Luminescence properties of chlorine molecules in glassy SiO 2 and optical fibre waveguides
2017
The support from Latvian Research Program IMIS 2, project “Photonics and materials for photonics” is acknowledged. K.K. was partially supported by the Collaborative Research Project of Materials and Structures Laboratory, Tokyo Institute of Technology. The publication costs of this article were covered by the Estonian Academy of Sciences and the University of Tartu.
Er3+-doped GeGaSbS glasses for mid-IR fibre laser application: Synthesis and rare earth spectroscopy
2008
International audience; With an infrared transparency extended to 10 µm, low multiphonon relaxation rates and suitable rare earth solubility, sulphide glasses in the Ge-Ga-Sb-S system allow radiative emission from rare earth ions in the mid-IR range. The Er3+ ion, widely studied in glass fibres for optical amplification at 1.5 µm, presents an interesting transition for mid-IR applications around 4.5 µm (4I9/2→ 4I11/2). Thus, the aim of this work is to evaluate the Er3+-doped Ge20Ga5Sb10S65 glass as a potential fibre laser source operating in the 3-5 µm mid-IR spectral region. For that purpose, absorption and emission spectra were recorded from visible to mid-IR and the radiative lifetimes o…
Ultraviolet-visible light-induced solarisation in silica-based optical fibres for indoor solar applications
2021
Abstract The transmission performances of pure- and doped-silica (a-SiO2) optical fibres are compared during the exposure to a high-power broadband light source approximating the solar spectrum. From the Gaussian decomposition of the attenuation spectra, we found that Al- and P-doped fibres show a fast solarisation effect which leads to transmission degradation in the ultraviolet-visible range. Similarly, Ge-doped fibres undergo photoinduced colour-centre formation which, however, does not prevent visible-light propagation. One of the two tested pure-silica fibres results completely unaffected by light exposure whereas the other shows an absorption band probably due to the presence of chlor…
Rare-earth doped silica optical fibres for ionizing radiation detection
2016
Scintillating silica optical fibre sensors have shown interesting results for ionizing radiation monitoring and therefore can be useful for dosimetry applications in medical field. In fact, they enable a remote, punctual and real-time dose assessment (Mones et al., 2008). In addition, the high radiation hardness that characterizes silica optical fibers, makes these systems promising for radiation detection in high energy physics experiments (Chiodini et al., 2014). This work aims to review the recent progresses in the development and characterization of rare-earth doped silica fibres. The radioluminescent and dosimetric properties of Ce, Eu, Yb and Pr-doped silica matrices are described and…
Size control of InAs∕InP(001) quantum wires by tailoring P∕As exchange
2004
The size and emission wavelength of self-assembled InAs∕InP(001) quantum wires (QWrs) is affected by the P∕As exchange process. In this work, we demonstrate by in situ stress measurements that P∕As exchange at the InAs∕InP interface depends on the surface reconstruction of the InAs starting surface and its immediate evolution when the arsenic cell is closed. Accordingly, the amount of InP grown on InAs by P∕As exchange increases with substrate temperature in a steplike way. These results allow us to engineer the size of the QWr for emission at 1.3 and 1.55 μm at room temperature by selecting the range of substrate temperatures in which the InP cap layer is grown.